Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL 5002 Weight 1000 g Color blue MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178)
Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) .
viac
Najlacnejší produkt
34,88 € | cdrmarket.cz
Máte lepší produkt vo vašom obchode?
Najlacnejší produkt
34,88 € | cdrmarket.cz
Máte lepší produkt vo vašom obchode?
Dostupné v
K dispozícii v iných krajinách
Čo hovoria obchody
cdrmarket.sk
Features Strong, high clarity, odour neutral and easy-to-print filament High impact strength Excellent flexibility Almost no warping or shrinkage Hydrophobic (does not absorb water) Food packaging grade pellets used Main applications: Concept modelling for mechanics, medical, food containers, transparent objects. TECHNICAL SPECIFICATIONS Diameter 2.85 mm ± 0.10 mm Roundness >95% RAL 5002 Weight 1000 g Color blue MATERIAL PROPERTIES Specific gravity 1.27g/cc (Test method: ISO 1183) MFR 190°C/2.16 kg 6.4 gr/10 min (Test method: ISO 1133) Tensile strength at yield 50 mPa Strain at yield 5% (Test method: ISO 527) Strain at break 23% (Test method: ISO 527) Tensile modulus 2020 MPa (Test method: ISO 527) Flexural modulus 2050 MPa (Test method: ISO 178) Flexural strength 69 MPa (Test method: ISO 178) Impact strength - Charpy method 23°C 8.1 kJ/m2 (Test method: ISO 179) Rockwell Hardness 105 (Test method: ASTM D785) Moisture absorption 1104 ppm (Test method: ISO 62) Printing temperature 240±10°C Heat deflection temperature 70°C (Test metod: ASTM 648) Transparency 90% (Test method: ASTM D1003) .